J. Ocean Eng. Technol. 2001;15(1):57-66.
The Elementary Study on the Development of a Sensor for Measurement of Steel Corrosion by Transient Electro-Magnetic (TEM) Method
TEM 법에 의한 철근 부식 측정 센서 개발에 대한 기초 연구
이상호,한정섭
동해대학교 건축공학과,동아대학교 토목·해양공학부
Key Words: Transient electro-magnetic method, Secondary electro motive force, Coincident loop configuration
핵심용어: 과도전자탐사법, 2차 기전력, 동일루프배열
Abstract
In order to measure steel corrosion in mortar by a transient electro-magnetic (TEM) Method, the development of the sensors have been studied. The sensors were made of enamelled wire with diameter of 0.25mm and Acril. The sensor configuration was used as a coincident loop type. The secondary electro motive force(EMF) was measured with SIROTEM III. The accelerator was equipped with the SIROTEM III. The accelerator permits the transmitter to turn off approximately 10~15 times faster than normal. The high resolution time series used for very shallow or high resistivity investigation was selected. The steels were embedded in mortar which were made from sand : cement : water ratio of 2 : 1: 0.5. The mortar specimen was 50cm long, 20cm wide and 10cm thick. To investigate steel corrosion in mortar, the sensors used were with 2$ imes$2$cm^2$(3, 6, 9$Omega$), 3$ imes$3$cm^2$(3, 6, 9$Omega$) and 6$ imes$6$cm^2$(3, 6, 9$Omega$). The obtained result obtained showed that the sensor 8(6$ imes$6$cm^2$, 6$Omega$) was the proper sensor for the measurement of steel corrosion in mortar.


ABOUT
ARTICLE CATEGORY

Browse all articles >

BROWSE ARTICLES
AUTHOR INFORMATION
Editorial Office
President O/T room No.1302, 13, Jungang-daero 180beon-gil, Dong-gu, Busan 48821, Korea
Tel: +82-51-759-0656    Fax: +82-51-759-0656    E-mail: ksoehj@ksoe.or.kr                

Copyright © 2019 by The Korean Society of Ocean Engineers. All rights reserved.

Developed in M2community

Close layer
prev next