Evaluation of J-R Curve and Tmat of SA 508C-3 Steel at Elevated Temperature |
Lim, Man-Bae;Cha, Gee-Jun; |
|
SA 508C-3강의 고온에서 J-R Curve 및 Tmat의 평가 |
임만배;차귀준; |
동아대학교 생산기술연구소;동명대학 가스냉동과; |
|
© 1998 The Korean Society of Ocean Engineers
Open access / Under a Creative Commons License
|
Keywords:
J-R Curve, Tearing Modulus, Unstable Crack, Growth, Crack Tip Open Displacement, Material Tearing Modulus |
핵심용어:
J-저항곡선, 찢어짐계수, 불안정 균열성장, 균열선단 개구변위, 재료의 찢어짐계수 |
Abstract |
In this study, the J-Resistance Curve and material tearing modulus of SA508-C3 steel, which is one of the used nuclear pressure vessel steel, are measured ar room temperature, $200^{circ}C$ and $300^{circ}C$ according to load ratio analysis and ASTM E813, ASTM E1152, respectively. It is observed that J-R curve and Tmat value decrease as the temperature level increase. Applicability of $T_j$ proposed by Paris et al as instability parameter for ductile material is investigated. It is concluded that results are the $T_j$ parameter may be used as a crack instability parameter. |
|