A Study on the Low Temperature Fracture Toughness of Ion-nitrided Ni-Cr-Mo Steel

J. Ocean Eng. Technol. 1987;1(2):101-112.

이온 실화처리한 Ni-Cr-Mo강의 저온파괴인성에 관한 연구

오세욱,윤한기,문인철

동아대학교 기계공학과,동의대학교 기계공학과,동아대학교 기계공학과

Keywords: $J_{IC}$, Ion-nitriding, unloading compliance, crack growth length, upper shelf region, low shelf region, transition region

Abstract

Fracture toughness characterization in the transition region is examined for heat-treated and ionnitrided Ni-Cr-Mo steel. After heat treatment for the specimens of Ni-Cr-Mo steel, organizations of specimens-specimens which are heat-treated and ion-nitrided for 4 hours at 500 .deg. C and 5 torr in 25%N/dub 2/-75%H/sub 2/mixed gas-, hardness variety, and X-ray diffraction pattern of the ion-nitriding compound layer are observed. Fracture toughenss test of unloading compliance method were conducted over the regions from room trmperature to -70.deg. C. The compound layer was consisted of r'=Fe/sub 4/N phase and ion-nitrided layer's depth was 200mm from surface. The transition regions of heat-treated and ion-nitrided specimens were about -30.deg. C and -50.deg. C, respectively. The transition region of ion-nitrided specimens is estimated less than that of heat-treated one, and this is the effect of ion-nitriding.